Boron Nitride Rod, BN Rod
Boron Nitride Rod, BN Rod
Boron nitride rod is a type of ceramic material made of boron and nitrogen atoms arranged in a crystal lattice structure. It is a high-performance material with excellent thermal and electrical insulation properties, high strength, and resistance to corrosion and wear.
Boron nitride rods come in different sizes and shapes, with diameters ranging from a few millimeters to several centimeters and lengths varying from a few centimeters to several meters. They can be machined into various geometries, including cylinders, tubes, blocks, and custom shapes.
Boron nitride rods find applications in various industries, including aerospace, electronics, metallurgy, and semiconductor manufacturing. They are used as high-temperature insulators, heat sinks, crucibles, nozzles, and furnace components. They can also be used as a replacement for graphite in some applications due to their high-temperature stability and non-wetting properties.
Boron Nitride Ceramics Specification
CG Material production formulations are developed to address the varied application problems in which ceramic components are commonly used. Many industrial applications push the envelope on specific requirements leading to the development of new formulations to successfully address them.
Item No. | Description | Purity | Lot Size |
CG-NI05-98 | Boron Nitride Powder Particle Size: 3 µm, 200 mesh or 325mesh |
BN > 98 %, B2O3 < 0.6%, Ca < 0.015%, Si < 0.12% |
100 kg 1000kg Customize |
CG-NI05-99 | Boron Nitride Powder Particle Size: 3 µm, 200 mesh or 325mesh |
BN > 99 %, B2O3 < 0.4%, Ca < 0.01%, Si < 0.10% |
100 kg 1000kg Customize |
Comparison of Boron Nitride Ceramics
Grade | BN-BO | BN-SZ | BN-AlN |
Compositions | BN>98% | BN+SiC+ZrO2 | BN+AIN |
Binder | B2O3 | / | AlBO3 |
Density | 2.1-2.2 g/cm3 | 2.3-3.0 g/cm3 | 2.5-2.6 g/cm3 |
25°C Volume Resistivity | >1013 Ω·cm | >1012 Ω·cm | >1014 Ω·cm |
Max. Service Temp. (°C) Oxygen; Inert Gas; High Vacuum |
900 2000 1800 |
900 1700 1700 |
900 2100 1900 |
Flexural Strength | 75 Mpa | 100 Mpa | 130 Mpa |
Compressive Strength | 100 Mpa | 300 Mpa | 250 Mpa |
Coefficient of Thermal Expansion 25-1000°C |
2.0 x 10–6/K | 4.0 x 10–6/K | 4.5 x 10–6/K |
Thermal Conductivity | 30 W/mK | 40 W/mK | 60 W/mK |
Boron Nitride Rod Available Materials
Material | Description | Availability |
BN99 | Hot pressed at high temperature (1900℃). Excellent corrosion resistance and thermal conductivity. Limited wear resistance Self-bonded and high purity (>99%) |
Machinable Blanks Finished Parts |
BNBO | General purpose material Bonded by boric oxide |
Finished Parts |
BNCB | Calcium borate bonded boron nitride Enhanced moisture resistance |
Finished Parts |
BN60 | BN 60%, SiO2 40% | Finished Parts |
BN40 | BN 40%, SiO2 60% | Finished Parts |
ZSBN | BN-45%, Zr2O3 45% | Finished Parts |
Boron Nitride Rod Advantages
BN rod is easily machinable. It has high performances:
– Low wettability to molten metal
– Low dielectric constant
– Relatively high dielectric strength
– Relatively high thermal conductivity with low thermal expansion
– Relatively high thermal shock resistance
– Extremely high working temperature with proper inert gas protection (>3000C has been recorded).
– Chemical Vapor Deposition (CVD)
Boron Nitride Rod Applications
Boron Nitride ceramic from CG Material can withstand high temperature in the high vacuum environment, plus it is chemically inert — it has excellent corrosion resistance and electrical resistance. Thus, Boron Nitride ceramic product is an ideal choice in a wide range of industries, such as:
-Evaporator Boats
-Nozzles for nonferrous metals metallurgy industry
-Electric insulators in the vacuum environment
-Insulators for high-temperature furnace
-Spacers for glass melting